X3CrNiMoAl13-8-2 1.4534 Turbine Blade Steel X3CrNiMoAl13-8-2 Round Bar 1.4534 Flat Bar
Description
Our company provides X3CrNiMoAl13-8-2 1.4534 A / S / Q + T / A + T Turbine Blade Steel X3CrNiMoAl13-8-2 Black / Bright / Rrough Turned / Grinding Round Bar 1.4534 Flat Bar.All of X3CrNiMoAl13-8-2 1.4534 A / S / Q + T / A + T Turbine Blade Steel X3CrNiMoAl13-8-2 Black / Bright / Rrough Turned / Grinding Round Bar 1.4534 Flat Bar conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Products Details
X3CrNiMoAl13-8-2 1.4534 A / S / Q + T / A + T Turbine Blade Steel X3CrNiMoAl13-8-2 Black / Bright / Rrough Turned / Grinding Round Bar 1.4534 Flat Bar
| Chemical Composition (weight%): |
| C | ≤ 0.05 |
| Si | ≤ 0.10 |
| Mn | ≤ 0.20 |
| P | ≤ 0.010 |
| S | ≤ 0.008 |
| Cr | 12.3 ~ 13.2 |
| Ni | 7.50 ~ 8.50 |
| Mo | 2.00 ~ 2.50 |
| Al | 0.90 ~ 1.35 |
| N | ≤ 0.01 |
| Mechanical Properties Under Final Heat Treatment: |
| Solution treatment temperature and cooling ways: 1050 +/-15℃ |
| Ageing teated: H1000, 540℃, 4h, air cooling |
| Tensile strength, σb≥/MPa | 1410 |
| Yield strength, σ0.2≥/MPa | 1312 |
| Elongation, δ≥(％) | 10.0 |
| Hardness |HRC | 43 |
| Ageing teated: H1025, 550℃, 4h, air cooling |
| Tensile strength, σb≥/MPa | 1275 |
| Yield strength, σ0.2≥/MPa | 1200 |
| Elongation, δ≥(％) | 11.0 |
| Hardness |HRC | 41 |
| Ageing teated: H1050, 565℃, 4h, air cooling |
| Tensile strength, σb≥/MPa | 1200 |
| Yield strength, σ0.2≥/MPa | 1135 |
| Elongation, δ≥(％) | 12.0 |
| Hardness |HRC | 40 |
| Ageing teated: H1100, 595℃, 4h, air cooling |
| Tensile strength, σb≥/MPa | 1030 |
| Yield strength, σ0.2≥/MPa | 930 |
| Elongation, δ≥(％) | 14.0 |
| Hardness |HRC | 34 |
| Ageing teated: H1150, 620℃, 4h, air cooling |
| Tensile strength, σb≥/MPa | 930 |
| Yield strength, σ0.2≥/MPa | 625 |
| Elongation, δ≥(％) | 14.0 |
| Hardness |HRC | 30 |
Applications:
X3CrNiMoAl13-8-2 1.4534 A / S / Q + T / A + T Turbine Blade Steel X3CrNiMoAl13-8-2 Black / Bright / Rrough Turned / Grinding Round Bar 1.4534 Flat Bar Chemical equipment,Mechanical parts used in the condition of corrosion resistance,Bolt and nut,Pressure vessel.
Equivalent Grade:
DIN X3CrNiMoAl13-8-2
1.4534
FAQ
Q: How do you control the quality?
A: We have professional inspectors to analyze the chemical composition of DIN 1.4534 13-8Mo Turbine Blade Steel DIN 1.4534 Round Bar 13-8Mo Flat Bar and test the finished products in strict accordance with the standards stipulated in the contract. In this process, the inner and outer surfaces, the appearance of both ends, bending, set length, outer diameter and Wall thickness will be checked one by one. You can rest assured that all products you receive from us are reliable.
Q: Do you accept customization?
A: Yes. If you have special requirements for products or packaging, we can make them for you.
Q: Can you accept trial orders?
A: Our MOQ is usually 1 ton. However, if you want to place an order as the start of our cooperation, we can accept smaller quantities at the first time. Of course, after the start, we will have further and longer cooperation.
Q: How do I get samples?
A: Free samples are available for your inspection and testing, DHL/FedEx/UPS accounts can be used for sampling, and the courier fee is borne by you.
Product Tags:
|
|
X3CrNiMoAl13-8-2 Round Bar Turbine Blade Steel 1.4534 Flat Bar Images
|